Investigation and Preparation of High Active Nano-MgO Thin SphericalMaterial

ISL OpenIR > 青海盐湖研究所知识仓储

	Investigation and Preparation of High Active Nano-MgO Thin SphericalMaterial
	Ren, Xiufeng; Zhou, Yuan; Sun, Qingguo; Nian, Hongen; Li, Xiang; Cao, Meng Meng
	2012
发表期刊	INTEGRATED FERROELECTRICS
ISSN	1058-4587
卷号	138 期号:*页码:128-136
关键词	High-temperature Spray Mgo Thin Sphere Nano-structure Bet Surface
摘要	High active MgO precursor was prepared by high-temperature spray thermal decomposition method using saturated MgCl2 as raw materials. And high active nano-MgO thin spherical materials were prepared by MgO precursor being calcined at different temperatures after multiple hydration, purification, and filtration. The XRD, TG, DSC and SEM were employed to characterize the phase structure and micro-morphology of spherical materials whose formation mechanism was researched. And its activity (average pore size and surface area) was detected by using BET-BJH of N-2 adsorption to get the optimum calcination temperature. The results showed that high active nano-MgO thin spherical material was periclase structure, its surface of nano-flake or rod-like, and thin sphere with diameter of 30 similar to 100 nm and aperture of 10 similar to 60 nm. The aperture was decreased while the surface area, microporous volume and surface activity were increased with preparation process were optimized, for example, calcination temperatures. Nano-MgO thin spherical material with a purity of 99.2 wt% was obtained at 900 degrees C. And BET surface area of nano-sphere reached a maximum value of 31.6 m(2)/g with nest-like structure of particle uniform dispersion and average aperture of 11.2 nm. Meanwhile, the maximum absorption of N-2 was gotten. High active MgO precursor was prepared by high-temperature spray thermal decomposition method using saturated MgCl2 as raw materials. And high active nano-MgO thin spherical materials were prepared by MgO precursor being calcined at different temperatures after multiple hydration, purification, and filtration. The XRD, TG, DSC and SEM were employed to characterize the phase structure and micro-morphology of spherical materials whose formation mechanism was researched. And its activity (average pore size and surface area) was detected by using BET-BJH of N-2 adsorption to get the optimum calcination temperature. The results showed that high active nano-MgO thin spherical material was periclase structure, its surface of nano-flake or rod-like, and thin sphere with diameter of 30 similar to 100 nm and aperture of 10 similar to 60 nm. The aperture was decreased while the surface area, microporous volume and surface activity were increased with preparation process were optimized, for example, calcination temperatures. Nano-MgO thin spherical material with a purity of 99.2 wt% was obtained at 900 degrees C. And BET surface area of nano-sphere reached a maximum value of 31.6 m(2)/g with nest-like structure of particle uniform dispersion and average aperture of 11.2 nm. Meanwhile, the maximum absorption of N-2 was gotten.
文献类型	期刊论文
条目标识符	http://ir.isl.ac.cn/handle/363002/2080
专题	青海盐湖研究所知识仓储盐湖资源与化学实验室支撑部门
推荐引用方式 GB/T 7714	Ren, Xiufeng,Zhou, Yuan,Sun, Qingguo,et al. Investigation and Preparation of High Active Nano-MgO Thin SphericalMaterial[J]. INTEGRATED FERROELECTRICS,2012,138(*):128-136.
APA	Ren, Xiufeng,Zhou, Yuan,Sun, Qingguo,Nian, Hongen,Li, Xiang,&Cao, Meng Meng.(2012).Investigation and Preparation of High Active Nano-MgO Thin SphericalMaterial.INTEGRATED FERROELECTRICS,138(*),128-136.
MLA	Ren, Xiufeng,et al."Investigation and Preparation of High Active Nano-MgO Thin SphericalMaterial".INTEGRATED FERROELECTRICS 138.*(2012):128-136.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
10584587.2012.688654（609KB）			开放获取	CC BY-NC-SA	浏览请求全文