| THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE | |
Huang, Qing; Li, Ying ; Chang, Chenggong; Zheng, Weixin; Wen, Jing; Dong, Jinmei; Man, Yangyang; Danchun, A.; Xiao, Xueying; Zhou, Yuan
| |
| 2019 | |
| 发表期刊 | CERAMICS-SILIKATY
 |
| ISSN | 0862-5468 |
| 卷号 | 63期号:4页码:347-355 |
| 摘要 | In this paper, the performance of magnesium oxychloride cement (MOC) in brine environment after the addition of an anti-corrosion admixture (Q101) was investigated. The compressive strength, compressive strength retention, crystal composition and microstructure were analysed in detail. The results show that the compressive strength of the MOC with the Q101 admixture maintains a high compressive strength of more than 100 MPa in air, and decreases slightly in the raw brine and the aging brine, but the decreases are not significant with the compressive strength of 80 MPa. This demonstrates the excellent salt brine resistance in brine environment of the MOC. One reason is that the high content of Mg2+ and Cl- in brine suppress the dissolution rate of main hydration product in the MOC. The other is the addition of an anti-corrosion additive that improves the salt brine resistance by about 30 %. However, the compressive strength and strength retention of the MOC after the raw brine immersion are higher than the aging brine immersion. The reason may be that the salts fill the surface and the pores in the samples that prevented water erosion to some extent. Meanwhile, the MOC pastes have the biggest compressive strength retention when the Q101 was up to 10 % over the long run. As a result, the optimum dosage of Q101 is 10 % in this experiment. |
| DOI | 10.13168/cs.2019.0030 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.isl.ac.cn/handle/363002/34081 |
| 专题 | 盐湖资源与化学实验室 中国科学院青海盐湖研究所 |
| 推荐引用方式 GB/T 7714 | Huang, Qing,Li, Ying,Chang, Chenggong,et al. THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE[J]. CERAMICS-SILIKATY,2019,63(4):347-355. |
| APA | Huang, Qing.,Li, Ying.,Chang, Chenggong.,Zheng, Weixin.,Wen, Jing.,...&Zhou, Yuan.(2019).THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE.CERAMICS-SILIKATY,63(4),347-355. |
| MLA | Huang, Qing,et al."THE COMPRESSIVE STRENGTH DEVELOPMENT OF MAGNESIUM OXYCHLORIDE CEMENT COMPRISING A COMPOSITE ADDITIVE IN BRINE".CERAMICS-SILIKATY 63.4(2019):347-355. |
| 条目包含的文件 | ||||||
| 文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
| THE COMPRESSIVE STRE（13372KB） | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | 浏览 请求全文 | |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论