Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage
Zhang, Hongtao1,3; Zhao, Youjing1,2; Li, Jingli1,2; Shi, Lijie1,2; Wang, Min1,2
2015-12-01
发表期刊HIGH TEMPERATURE MATERIALS AND PROCESSES
卷号34期号:8页码:839-846
关键词Solar Energy Materials Purification Thermal Properties Molten Nitrate Salts
摘要This paper focuses on thermal stability of molten salts, operating temperature range and latent heat of molten salts at a high temperature. In this experiment, multi-component molten salts (purified Solar Salt) composed of purified NaNO3 and purified KNO3 were prepared by statical mixing method. Compared with unpurified Solar Salt, purified Solar Salt had a higher thermal stability. The optimal temperature would be increased from 500 degrees C to 550 degrees C, and the upper limitation temperature increases from 577.5 degrees C to 593.7 degrees C. Meanwhile, thermal stability and thermal cycling analysis showed the purified Solar Salt had a lower melting point and the deterioration time of molten salts was reduced. The melting point of purified Solar Salt decreases sharply to 223.8 degrees C and the latent heat increases from 74.39 J/g to 80.79 J/g. Besides, the XRD and chemical analysis test indicated that the degree of degradation reduced and the thermal storage efficiency of purified Solar Salt was improved.
语种英语
引用统计
文献类型期刊论文
条目标识符http://ir.isl.ac.cn/handle/363002/5322
专题青海盐湖研究所知识仓储
中国科学院青海盐湖研究所
作者单位1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China
2.Chinese Acad Sci, Key Lab Salt Lake Resources & Chem, Qinghai 810008, Peoples R China
3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
推荐引用方式
GB/T 7714
Zhang, Hongtao,Zhao, Youjing,Li, Jingli,et al. Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage[J]. HIGH TEMPERATURE MATERIALS AND PROCESSES,2015,34(8):839-846.
APA Zhang, Hongtao,Zhao, Youjing,Li, Jingli,Shi, Lijie,&Wang, Min.(2015).Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage.HIGH TEMPERATURE MATERIALS AND PROCESSES,34(8),839-846.
MLA Zhang, Hongtao,et al."Preparation and Thermal Properties of High-Purified Molten Nitrate Salt Materials with Heat Transfer and Storage".HIGH TEMPERATURE MATERIALS AND PROCESSES 34.8(2015):839-846.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhang, Hongtao]的文章
[Zhao, Youjing]的文章
[Li, Jingli]的文章
百度学术
百度学术中相似的文章
[Zhang, Hongtao]的文章
[Zhao, Youjing]的文章
[Li, Jingli]的文章
必应学术
必应学术中相似的文章
[Zhang, Hongtao]的文章
[Zhao, Youjing]的文章
[Li, Jingli]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。