Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process

ISL OpenIR > 青海盐湖研究所知识仓储

	Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process
	Li, Shuangbin 1,2; Yao, Ying1 ; Jia, Yongzhong1 ; Jing, Yan1 ; Sun, Jinhe1 ; Xie, Shaolei1
	2015-04-04
发表期刊	FERROELECTRICS
卷号	478 期号:1 页码:127-131
关键词	Tetragonal Phase Hexagonal Phase Barium Titanate Microstructure
摘要	BaTiO3 (BT) ceramics are prepared above 2000 degrees C by direct current arc discharge plasma process in argon atmosphere. The results show the formation of the perovskite structure. However, the coexisting of tetragonal phase and hexagonal phase is found in the structure. It is also found that a small amount of BaTi4O9 compound appears. With the sintering temperature increasing, the structure becomes more homogeneous because of interdiffusion of constituent ions and phase transition. The hexagonal phase gradually disappears and BaTi4O9 compound could also be traced.
语种	英语
引用统计
文献类型	期刊论文
条目标识符	http://ir.isl.ac.cn/handle/363002/6134
专题	青海盐湖研究所知识仓储盐湖资源综合利用工程技术中心
作者单位	1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Key Lab Salt Lake Resources & Chem, Xining, Peoples R China 2.Univ Chinese Acad Sci, Beijing, Peoples R China
推荐引用方式 GB/T 7714	Li, Shuangbin,Yao, Ying,Jia, Yongzhong,et al. Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process[J]. FERROELECTRICS,2015,478(1):127-131.
APA	Li, Shuangbin,Yao, Ying,Jia, Yongzhong,Jing, Yan,Sun, Jinhe,&Xie, Shaolei.(2015).Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process.FERROELECTRICS,478(1),127-131.
MLA	Li, Shuangbin,et al."Phase Formation and Microstructure of BaTiO3 Ceramics Prepared by Direct Current Arc Discharge Process".FERROELECTRICS 478.1(2015):127-131.