Preparation and thermal energy storage studies of CH3COONa center dot 3H(2)O-KCl composites salt system with enhanced phase change performance | |
Li, Xiang1,2,3; Zhou, Yuan1,3; Nian, Hongen1,2,3; Zhu, Fayan1,3; Ren, Xiufeng1,2,3; Dong, Ouyang1,3; Hai, Chunxi1,3; Shen, Yue1,3; Zeng, Jinbo1,3 | |
2016-06-05 | |
发表期刊 | APPLIED THERMAL ENGINEERING |
卷号 | 102页码:708-715 |
关键词 | Phase Change Material (Pcm) Ch3coona Center Dot 3h(2)O-kcl Composites Salt System Al2o3 Nanoparticles Nucleating Agent Supercooling |
摘要 | The phase change performance of the CH3COONa center dot 3H(2)O-KCl composites salt system with Al2O3 nanoparticles and carboxyl methyl cellulose (CMC) were investigated in this paper. The CH3COONa center dot 3H(2)O-KCl composite salt system was prepared by adding KCI (at 2, 4, 6, 8, and 10 wt.%) to CH3COONa center dot 3H(2)O, respectively. Al2O3 nanoparticles were proposed as the nucleating agent and CMC was selected as a thickening agent for the CH3COONa center dot 3H(2)O-8 wt.%KCl composites salt system. The results show CH3COONa.3H(2)O-8 wt.%KCl composites salt system with 1 wt.% Al2O3 nanoparticles and 4 wt.% CMC, in which almost no supercoiling phenomenon occurs. After 50 cycles of the melting-freezing cycle test, aluminum oxide is uniformly dispersed in SAT composites matrix, the latent heat remained constant at about 232.29 J/g. The maximum deviations of latent heat of composites CH3COONa center dot 3H(2)O-8 wt.%KCl with 1 wt.% Al2O3 nanoparticles and 4 wt.% CMC before and after the fifty-run-recycling test are only 3.6%. (C) 2016 Elsevier Ltd. All rights reserved. |
语种 | 英语 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.isl.ac.cn/handle/363002/6335 |
专题 | 青海盐湖研究所知识仓储 盐湖资源与化学实验室 |
作者单位 | 1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Key Lab Salt Lake Resources Chem Qinghai Prov, Xining 810008, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Xiang,Zhou, Yuan,Nian, Hongen,et al. Preparation and thermal energy storage studies of CH3COONa center dot 3H(2)O-KCl composites salt system with enhanced phase change performance[J]. APPLIED THERMAL ENGINEERING,2016,102:708-715. |
APA | Li, Xiang.,Zhou, Yuan.,Nian, Hongen.,Zhu, Fayan.,Ren, Xiufeng.,...&Zeng, Jinbo.(2016).Preparation and thermal energy storage studies of CH3COONa center dot 3H(2)O-KCl composites salt system with enhanced phase change performance.APPLIED THERMAL ENGINEERING,102,708-715. |
MLA | Li, Xiang,et al."Preparation and thermal energy storage studies of CH3COONa center dot 3H(2)O-KCl composites salt system with enhanced phase change performance".APPLIED THERMAL ENGINEERING 102(2016):708-715. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论