Damping Capacities of Porous Mg-based Ternary Alloys Prepared by a Stir-casting Method
Wang, Yun-si ; Niu, Rui-long ; Yan, Fang-jia ; Duan, Dong-ping ; Yang, Xue-min
2018-06-15
Source PublicationCHEMISTRYSELECT
AbstractA new approach for preparing porous Mg-Al-Sr ternary alloys has been proposed using stir-casting method. Experimental results indicate that porosity and pore diameters have close relation with chemical composition of Mg-based ternary alloys. The proposed formation mechanism of pores in Mg-based ternary alloys can be described as that the oxidization reaction between [Sr] and O-2 in air provides enough heat source to vaporize small amount of Mg-based ternary alloys, while the vaporized products promote formation of embodied pores with various sizes and shapes in Mg-based ternary alloys during solidification process. Meanwhile, some oxides in shape of sheets will be formed and precipitated, while other oxides will also be precipitated on surface of pore wall during cooling. Moreover, the measured damping capacities expressed by internal friction tan indicate that changing temperature from ambient temperature to 343K cannot cause a large effect on damping capacities, however the inverse V-shape plots of damping capacities against temperature from 343 to 573K are obtained. In addition, increasing vibration frequencies can result in a decrease of internal friction tan. The optimized chemical composition as 50%Mg-47%Al-3%Sr and 50%Mg-45%Al-5%Sr are recommended for Mg-based ternary alloys with greater porosity and higher damping performance under temperature and vibration frequency.
PublisherWILEY-V C H VERLAG GMBH
Document Type期刊论文
Identifierhttp://ir.isl.ac.cn/handle/363002/7192
Collection中国科学院青海盐湖研究所
Recommended Citation
GB/T 7714
Wang, Yun-si,Niu, Rui-long,Yan, Fang-jia,et al. Damping Capacities of Porous Mg-based Ternary Alloys Prepared by a Stir-casting Method[J]. CHEMISTRYSELECT,2018.
APA Wang, Yun-si,Niu, Rui-long,Yan, Fang-jia,Duan, Dong-ping,&Yang, Xue-min.(2018).Damping Capacities of Porous Mg-based Ternary Alloys Prepared by a Stir-casting Method.CHEMISTRYSELECT.
MLA Wang, Yun-si,et al."Damping Capacities of Porous Mg-based Ternary Alloys Prepared by a Stir-casting Method".CHEMISTRYSELECT (2018).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang, Yun-si]'s Articles
[Niu, Rui-long]'s Articles
[Yan, Fang-jia]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang, Yun-si]'s Articles
[Niu, Rui-long]'s Articles
[Yan, Fang-jia]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang, Yun-si]'s Articles
[Niu, Rui-long]'s Articles
[Yan, Fang-jia]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.