题名: Preparation and Characterization of LiBF4 by Gradient HeatingDehydration
作者: 周园 ;  Zhang Xinyue ;  年洪恩 ;  Pang Yuna ;  Wang Hongbin
刊名: ACTA CHIMICA SINICA
出版日期: 2010
卷号: 68, 期号:14, 页码:1399-1403
英文摘要: LiBF4 was prepared via aqueous solution process and its properties were examined by X-ray diffraction (XRD), IR, and thermogravimetry and differential thermogravimetry (TG-DTG). H3BO3, HF and Li2CO3 were used as starting materials to prepare LiBF4 solution, followed by concentrating, crystallizing and dehydrating to obtain LiBF4. The incomplete dehydration caused by traditional rapid heating was avoided through gradient heating dehydration. The obtained LiBF4 crystal belongs to the hexagonal system with space group P3(1)2(1), confirmed by its XRD spectrum which conformed to powder diffraction file (PDF) card 00-040-1431. The infrared absorption bands of the obtained LiBF4 were observed, one band located at 1050 cm(-1), and splitted off two bands which are located at 1055 and 1038 cm(-1); the other band located at 650 cm(-1); attributed to nu(3) (as) vibration and delta(3) (s) vibration, respectively. In TG-DTG spectrum, a weak decomposition peak was observed at 341.31 K and a strong decomposition peak appeared at 516.48 K, the weight loss rate was 72.33%. The decomposition was regarded as the LiBF4 decomposed into LiF and BF3. LiBF4 was prepared via aqueous solution process and its properties were examined by X-ray diffraction (XRD), IR, and thermogravimetry and differential thermogravimetry (TG-DTG). H3BO3, HF and Li2CO3 were used as starting materials to prepare LiBF4 solution, followed by concentrating, crystallizing and dehydrating to obtain LiBF4. The incomplete dehydration caused by traditional rapid heating was avoided through gradient heating dehydration. The obtained LiBF4 crystal belongs to the hexagonal system with space group P3(1)2(1), confirmed by its XRD spectrum which conformed to powder diffraction file (PDF) card 00-040-1431. The infrared absorption bands of the obtained LiBF4 were observed, one band located at 1050 cm(-1), and splitted off two bands which are located at 1055 and 1038 cm(-1); the other band located at 650 cm(-1); attributed to nu(3) (as) vibration and delta(3) (s) vibration, respectively. In TG-DTG spectrum, a weak decomposition peak was observed at 341.31 K and a strong decomposition peak appeared at 516.48 K, the weight loss rate was 72.33%. The decomposition was regarded as the LiBF4 decomposed into LiF and BF3.
收录类别: SCI
Citation statistics: 
内容类型: 期刊论文
URI标识: http://ir.isl.ac.cn/handle/363002/1909
Appears in Collections:青海盐湖研究所知识仓储(2014年之前)_期刊论文

Files in This Item:

There are no files associated with this item.


Recommended Citation:
Zhou Yuan,Zhang Xinyue,Nian Hongen,et al. Preparation and Characterization of LiBF4 by Gradient HeatingDehydration[J]. ACTA CHIMICA SINICA,2010,68(14):1399-1403.
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Zhou Yuan]'s Articles
 [Zhang Xinyue]'s Articles
 [Nian Hongen]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Zhou Yuan]‘s Articles
 [Zhang Xinyue]‘s Articles
 [Nian Hongen]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2016  中国科学院青海盐湖研究所 - Feedback
Powered by CSpace