Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells

ISL OpenIR > 青海盐湖研究所知识仓储

	Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells
	Zhang, Jingchang 1,2; Fu, Zhenhai1,3 ; Iv, Qian 2; Yang, Xiuying 2; Cao, Weiliang 1,2
	2012-09-01
发表期刊	JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
卷号	63 期号:3 页码:554-562
关键词	N-zn/tio2 Anode Films Ticl4 Treatment Co-sensitization Dye-sensitized Solar Cell
摘要	Nanocrystalline N-Zn/TiO2 anode films were prepared by doping element N and Zn. These element-doped films have a better performance in dye-sensitized solar cell than the non-doped film. The test shows that the best thickness of N-Zn/TiO2 anode film is 13.5 mu m. UV-Visible measurements show that there is a complementarity in ultraviolet-visible absorbance range between P3OT and N719, both are used as dyes in this study, the former is prepared and the latter is commercially available. SEM shows a significant mass increase of anode film after treated with TiCl4. Solar cells based on N-Zn/TiO2 anode film with TiCl4 treatment was firstly co-sensitized by N719/P3OT. A solar-to-electric energy conversion efficiency of 3.54 % was obtained. Compared with the traditional dye-sensitized solar cell, the photoelectric conversion efficiency, V (oc) and J (sc) have been increased.
语种	英语
引用统计
文献类型	期刊论文
条目标识符	http://ir.isl.ac.cn/handle/363002/5637
专题	青海盐湖研究所知识仓储中国科学院青海盐湖研究所盐湖资源与化学实验室
作者单位	1.Beijing Univ Chem Technol, Inst Modern Catalysis, State Key Lab Chem Resource Engn, Beijing 100029, Peoples R China 2.Hainan Inst Sci & Technol, Haikou 571126, Peoples R China 3.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China
推荐引用方式 GB/T 7714	Zhang, Jingchang,Fu, Zhenhai,Iv, Qian,et al. Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells[J]. JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY,2012,63(3):554-562.
APA	Zhang, Jingchang,Fu, Zhenhai,Iv, Qian,Yang, Xiuying,&Cao, Weiliang.(2012).Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells.JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY,63(3),554-562.
MLA	Zhang, Jingchang,et al."Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells".JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY 63.3(2012):554-562.