Preparation and Characterization of LiBF4 by Gradient Heating Dehydration
Zhou Yuan1; Zhang Xinyue1,2,3; Nian Hongen1; Pang Yuna1,2; Wang Hongbin1,2
2010-07-28
Source PublicationACTA CHIMICA SINICA
Volume68Issue:14Pages:1399-1403
SubtypeArticle
AbstractLiBF4 was prepared via aqueous solution process and its properties were examined by X-ray diffraction (XRD), IR, and thermogravimetry and differential thermogravimetry (TG-DTG). H3BO3, HF and Li2CO3 were used as starting materials to prepare LiBF4 solution, followed by concentrating, crystallizing and dehydrating to obtain LiBF4. The incomplete dehydration caused by traditional rapid heating was avoided through gradient heating dehydration. The obtained LiBF4 crystal belongs to the hexagonal system with space group P3(1)2(1), confirmed by its XRD spectrum which conformed to powder diffraction file (PDF) card 00-040-1431. The infrared absorption bands of the obtained LiBF4 were observed, one band located at 1050 cm(-1), and splitted off two bands which are located at 1055 and 1038 cm(-1); the other band located at 650 cm(-1); attributed to nu(3) (as) vibration and delta(3) (s) vibration, respectively. In TG-DTG spectrum, a weak decomposition peak was observed at 341.31 K and a strong decomposition peak appeared at 516.48 K, the weight loss rate was 72.33%. The decomposition was regarded as the LiBF4 decomposed into LiF and BF3.
KeywordLibf4 Electrolyte Lithium-ion Battery Lithium Salt Aqueous Solution Process
WOS HeadingsScience & Technology ; Physical Sciences
WOS KeywordLOW-TEMPERATURE PERFORMANCE ; LITHIUM-ION BATTERIES ; THERMAL-BEHAVIOR ; ELECTROLYTE ; LI ; TETRAFLUOROBORATE ; CORROSION ; ALUMINUM ; SALT
Indexed BySCI
Language英语
WOS Research AreaChemistry
WOS SubjectChemistry, Multidisciplinary
WOS IDWOS:000281685100009
Citation statistics
Document Type期刊论文
Identifierhttp://ir.isl.ac.cn/handle/363002/5939
Collection青海盐湖研究所知识仓储
盐湖资源与化学实验室
Affiliation1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China
2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China
3.Chinese Acad Sci, Inst Chem, Beijing 100190, Peoples R China
Recommended Citation
GB/T 7714
Zhou Yuan,Zhang Xinyue,Nian Hongen,et al. Preparation and Characterization of LiBF4 by Gradient Heating Dehydration[J]. ACTA CHIMICA SINICA,2010,68(14):1399-1403.
APA Zhou Yuan,Zhang Xinyue,Nian Hongen,Pang Yuna,&Wang Hongbin.(2010).Preparation and Characterization of LiBF4 by Gradient Heating Dehydration.ACTA CHIMICA SINICA,68(14),1399-1403.
MLA Zhou Yuan,et al."Preparation and Characterization of LiBF4 by Gradient Heating Dehydration".ACTA CHIMICA SINICA 68.14(2010):1399-1403.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhou Yuan]'s Articles
[Zhang Xinyue]'s Articles
[Nian Hongen]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhou Yuan]'s Articles
[Zhang Xinyue]'s Articles
[Nian Hongen]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhou Yuan]'s Articles
[Zhang Xinyue]'s Articles
[Nian Hongen]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.