Performance evaluation of solidification of Cr3+ or Ni2+ in industrial wastewater with Sorrel's cement
Wu, Chengyou1; Zhang, Huifang2; Yu, Hongfa1,3
2017-03-01
发表期刊DESALINATION AND WATER TREATMENT
卷号68页码:361-368
文章类型Article
摘要Sorrel's cement has been investigated as a means of solidifying Cr3+ or Ni2+ in wastewater. The setting time, compressive strength, water resistance, and leaching toxicity of solidified products of Sorrel's cement with Cr3+ or Ni2+ have been studied comprehensively to assess the applicability of Sorrel's cement in industrial wastewater treatment. Analysis of solidified products of Sorrel's cement with Cr3+ or Ni2+ was conducted by XRD, TG, FTIR, and SEM. Results demonstrate that the solidification of Cr3+ or Ni2+ inhibits the hydration process of Sorrel's cement. Results also indicate the inhibition of 5Mg(OH)(2)center dot MgCl2 center dot 5H(2)O (5 phase) formation, which is the main strength phase in Sorrel's cement, subsequently leading to the reduction of compressive strength of Sorrel's cement from 136 MPa to 67 MPa; the reduced compressive strength still far exceeds the standard value of 7 MPa. Additionally, the water resistance of cement solidified products also meets the requirements specified in the related standard. The leaching toxicity of Cr3+ or Ni2+ from solidified products of Sorrel's cement was also evaluated. The highest observed leaching concentration from solidified products reached 0.110 mg/L and 0.311 mg/L for Cr3+ and Ni2+, respectively, indicating that Sorrel's cement solidified products with Cr3+ or Ni2+ exhibits an acceptably low leaching toxicity.
关键词Sorrel's Cement Solidification Cr3++ Ni2++ Leaching Toxicity Compressive Strength Water Resistance
WOS标题词Science & Technology ; Technology ; Physical Sciences
关键词[WOS]MAGNESIUM OXYCHLORIDE CEMENT ; HEAVY-METALS ; FLY-ASH ; STRENGTH ; SOILS ; ZN
收录类别SCI
语种英语
WOS研究方向Engineering ; Water Resources
WOS类目Engineering, Chemical ; Water Resources
WOS记录号WOS:000403569900040
引用统计
文献类型期刊论文
条目标识符http://ir.isl.ac.cn/handle/363002/6227
专题青海盐湖研究所知识仓储
盐湖资源综合利用工程技术中心
作者单位1.Qinghai Univ, Sch Civil Engn, Xining 810016, Peoples R China
2.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China
3.Nanjing Univ Aeronaut & Astronaut, Dept Civil Engn, Nanjing 210016, Jiangsu, Peoples R China
推荐引用方式
GB/T 7714
Wu, Chengyou,Zhang, Huifang,Yu, Hongfa. Performance evaluation of solidification of Cr3+ or Ni2+ in industrial wastewater with Sorrel's cement[J]. DESALINATION AND WATER TREATMENT,2017,68:361-368.
APA Wu, Chengyou,Zhang, Huifang,&Yu, Hongfa.(2017).Performance evaluation of solidification of Cr3+ or Ni2+ in industrial wastewater with Sorrel's cement.DESALINATION AND WATER TREATMENT,68,361-368.
MLA Wu, Chengyou,et al."Performance evaluation of solidification of Cr3+ or Ni2+ in industrial wastewater with Sorrel's cement".DESALINATION AND WATER TREATMENT 68(2017):361-368.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Wu, Chengyou]的文章
[Zhang, Huifang]的文章
[Yu, Hongfa]的文章
百度学术
百度学术中相似的文章
[Wu, Chengyou]的文章
[Zhang, Huifang]的文章
[Yu, Hongfa]的文章
必应学术
必应学术中相似的文章
[Wu, Chengyou]的文章
[Zhang, Huifang]的文章
[Yu, Hongfa]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。