Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property
Zhang, Bo1,2,3; Feng, Haitao1,3; Lin, Feng1,2; Wang, Yabin1,3; Wang, Liping1,2; Dong, Yaping1,3; Li, Wu1,3
2016-08-15
发表期刊APPLIED SURFACE SCIENCE
卷号378页码:388-396
关键词Superhydrophobic Iron Substrate Black Chromium Stearic Acid Corrosion Resistance
摘要The fabrication of superhydrophobic surface on iron substrate is carried out through 20 min black chromium electrodeposition, followed by immersing in 0.05 M ethanolic stearic acid solution for 12 h. The resultant superhydrophobic complex film is characterized by scanning electron microscope (SEM), disperse Spectrometer (EDS), atomic force microscope (AFM), water contact angle (CA), sliding angle (SA) and X-ray photoelectron spectroscope (XPS), and its corrosion resistance property is measured with cyclic voltammetry (CV), linear polarization and electrochemical impedance spectroscopy (EIS). The results show that the fabricated superhydrophobic film has excellent water repellency (CA, 158.8; SA, 2.1) and significantly high corrosion resistance (1.31 x 10(6) Omega cm(-2)) and excellent corrosion protection efficiency (99.94%). (C) 2016 Elsevier B.V. All rights reserved.
语种英语
引用统计
文献类型期刊论文
条目标识符http://ir.isl.ac.cn/handle/363002/6323
专题青海盐湖研究所知识仓储
盐湖资源综合利用工程技术中心
作者单位1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Qinghai, Peoples R China
2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
3.Chinese Acad Sci, Key Lab Comprehens & Highly Efficient Utilizat Sa, Xining 810008, Qinghai, Peoples R China
推荐引用方式
GB/T 7714
Zhang, Bo,Feng, Haitao,Lin, Feng,et al. Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property[J]. APPLIED SURFACE SCIENCE,2016,378:388-396.
APA Zhang, Bo.,Feng, Haitao.,Lin, Feng.,Wang, Yabin.,Wang, Liping.,...&Li, Wu.(2016).Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property.APPLIED SURFACE SCIENCE,378,388-396.
MLA Zhang, Bo,et al."Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property".APPLIED SURFACE SCIENCE 378(2016):388-396.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhang, Bo]的文章
[Feng, Haitao]的文章
[Lin, Feng]的文章
百度学术
百度学术中相似的文章
[Zhang, Bo]的文章
[Feng, Haitao]的文章
[Lin, Feng]的文章
必应学术
必应学术中相似的文章
[Zhang, Bo]的文章
[Feng, Haitao]的文章
[Lin, Feng]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。