Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property

ISL OpenIR > 青海盐湖研究所知识仓储

	Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property
	Zhang, Bo1,2,3 ; Feng, Haitao1,3 ; Lin, Feng 1,2; Wang, Yabin 1,3; Wang, Liping 1,2; Dong, Yaping1,3 ; Li, Wu1,3
	2016-08-15
发表期刊	APPLIED SURFACE SCIENCE
卷号	378 页码:388-396
关键词	Superhydrophobic Iron Substrate Black Chromium Stearic Acid Corrosion Resistance
摘要	The fabrication of superhydrophobic surface on iron substrate is carried out through 20 min black chromium electrodeposition, followed by immersing in 0.05 M ethanolic stearic acid solution for 12 h. The resultant superhydrophobic complex film is characterized by scanning electron microscope (SEM), disperse Spectrometer (EDS), atomic force microscope (AFM), water contact angle (CA), sliding angle (SA) and X-ray photoelectron spectroscope (XPS), and its corrosion resistance property is measured with cyclic voltammetry (CV), linear polarization and electrochemical impedance spectroscopy (EIS). The results show that the fabricated superhydrophobic film has excellent water repellency (CA, 158.8; SA, 2.1) and significantly high corrosion resistance (1.31 x 10(6) Omega cm(-2)) and excellent corrosion protection efficiency (99.94%). (C) 2016 Elsevier B.V. All rights reserved.
语种	英语
引用统计
文献类型	期刊论文
条目标识符	http://ir.isl.ac.cn/handle/363002/6323
专题	青海盐湖研究所知识仓储盐湖资源综合利用工程技术中心
作者单位	1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Qinghai, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Chinese Acad Sci, Key Lab Comprehens & Highly Efficient Utilizat Sa, Xining 810008, Qinghai, Peoples R China
推荐引用方式 GB/T 7714	Zhang, Bo,Feng, Haitao,Lin, Feng,et al. Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property[J]. APPLIED SURFACE SCIENCE,2016,378:388-396.
APA	Zhang, Bo.,Feng, Haitao.,Lin, Feng.,Wang, Yabin.,Wang, Liping.,...&Li, Wu.(2016).Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property.APPLIED SURFACE SCIENCE,378,388-396.
MLA	Zhang, Bo,et al."Superhydrophobic surface fabricated on iron substrate by black chromium electrodeposition and its corrosion resistance property".APPLIED SURFACE SCIENCE 378(2016):388-396.