Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion
Zhang, Xinxing1,2,3; Li, Xiang1,3; Zhou, Yuan1,3; Hai, Chunxi1,3; Shen, Yue1,3; Ren, Xiufeng1,3; Zeng, Jinbo1,3
2018
发表期刊RSC ADVANCES
卷号8期号:2页码:1022-1029
文章类型Article
摘要The phase change enthalpy, thermal conductivity, thermal stability and thermal reliability of a novel reduced graphene oxide (r-GO) containing phase change material (PCM) r-GO/CaCl2 center dot 6H(2)O were investigated. The material was made by the aqueous dispersion of r-GO and calcium chloride dihydrate (CaCl2 center dot 2H(2)O) according to the mass ratio of CaCl2 and crystal water in CaCl2 center dot 6H(2)O. The thermal conductivity of the phase change material increased by similar to 80% when using similar to 0.018% (by weight) of r-GO with a similar to 2.7% decrease of enthalpy (i.e., storage capacity), while using similar to 0.018% of graphite led to an increase of thermal conductivity by similar to 14% and a decrease of enthalpy by similar to 5.6%. Additionally, the surface active agent for dispersing r-GO had the extra function of enhancing the system stability and reliability. The decomposing temperatures of r-GO/CaCl2 center dot H2O were higher than those of CaCl2 center dot 6H(2)O. After 100 cycles, the melting and crystallizing enthalpies of r-GO/CaCl2 center dot 6H(2)O decreased to 178.4 J g(-1) and 150.7 J g(-1) from 180.6 J g(-1) and 153.7 J g(-1), dropping by 1.2% and 2.0%, respectively, while for CaCl2 center dot 6H(2)O they decreased to 178.9 J g(-1) and 147.8 J g(-1) from 185.6 J g(-1) and 161.8 J g(-1), dropping by 3.7% and 8.7%, respectively. The thermal conductivity enhancement of CaCl2 center dot 6H(2)O with r-GO was markedly superior compared to that with graphite and other thermal conductive additives reported in previous literature, and the provided method (i.e., preparing aqueous dispersions of additives firstly and synthesizing hydrated salt PCMs with corresponding salts subsequently) was also applicable for other functional additives that cannot be directly dispersed well to modify the thermal properties of hydrated salt PCM systems.
WOS标题词Science & Technology ; Physical Sciences
关键词[WOS]PHASE-CHANGE MATERIALS ; LATENT-HEAT STORAGE ; ENERGY-STORAGE ; RAMAN-SPECTROSCOPY ; GRAPHITE ; CARBON ; COMPOSITES ; BUILDINGS ; BEHAVIOR
收录类别SCI
语种英语
WOS研究方向Chemistry
WOS类目Chemistry, Multidisciplinary
WOS记录号WOS:000419347900050
引用统计
被引频次:1[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.isl.ac.cn/handle/363002/6374
专题青海盐湖研究所知识仓储
作者单位1.Chinese Acad Sci, Key Lab Comprehens & Highly Efficient Utilizat Sa, Xining 810008, Qinghai, Peoples R China
2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
3.Key Lab Salt Lake Resources Chem Qinghai Prov, Xining 810008, Qinghai, Peoples R China
推荐引用方式
GB/T 7714
Zhang, Xinxing,Li, Xiang,Zhou, Yuan,et al. Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion[J]. RSC ADVANCES,2018,8(2):1022-1029.
APA Zhang, Xinxing.,Li, Xiang.,Zhou, Yuan.,Hai, Chunxi.,Shen, Yue.,...&Zeng, Jinbo.(2018).Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion.RSC ADVANCES,8(2),1022-1029.
MLA Zhang, Xinxing,et al."Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion".RSC ADVANCES 8.2(2018):1022-1029.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhang, Xinxing]的文章
[Li, Xiang]的文章
[Zhou, Yuan]的文章
百度学术
百度学术中相似的文章
[Zhang, Xinxing]的文章
[Li, Xiang]的文章
[Zhou, Yuan]的文章
必应学术
必应学术中相似的文章
[Zhang, Xinxing]的文章
[Li, Xiang]的文章
[Zhou, Yuan]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。