Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion

doi:10.1039/c7ra10632g

ISL OpenIR > 青海盐湖研究所知识仓储

	Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion
	Zhang, Xinxing; Li, Xiang; Zhou, Yuan; Hai, Chunxi; Shen, Yue; Ren, Xiufeng; Zeng, Jinbo
第一作者	Zhang, Xinxing
	2018
发表期刊	RSC ADVANCES
ISSN	2046-2069
卷号	8 期号:2 页码:1022-1029
摘要	The phase change enthalpy, thermal conductivity, thermal stability and thermal reliability of a novel reduced graphene oxide (r-GO) containing phase change material (PCM) r-GO/CaCl2 center dot 6H(2)O were investigated. The material was made by the aqueous dispersion of r-GO and calcium chloride dihydrate (CaCl2 center dot 2H(2)O) according to the mass ratio of CaCl2 and crystal water in CaCl2 center dot 6H(2)O. The thermal conductivity of the phase change material increased by similar to 80% when using similar to 0.018% (by weight) of r-GO with a similar to 2.7% decrease of enthalpy (i.e., storage capacity), while using similar to 0.018% of graphite led to an increase of thermal conductivity by similar to 14% and a decrease of enthalpy by similar to 5.6%. Additionally, the surface active agent for dispersing r-GO had the extra function of enhancing the system stability and reliability. The decomposing temperatures of r-GO/CaCl2 center dot H2O were higher than those of CaCl2 center dot 6H(2)O. After 100 cycles, the melting and crystallizing enthalpies of r-GO/CaCl2 center dot 6H(2)O decreased to 178.4 J g(-1) and 150.7 J g(-1) from 180.6 J g(-1) and 153.7 J g(-1), dropping by 1.2% and 2.0%, respectively, while for CaCl2 center dot 6H(2)O they decreased to 178.9 J g(-1) and 147.8 J g(-1) from 185.6 J g(-1) and 161.8 J g(-1), dropping by 3.7% and 8.7%, respectively. The thermal conductivity enhancement of CaCl2 center dot 6H(2)O with r-GO was markedly superior compared to that with graphite and other thermal conductive additives reported in previous literature, and the provided method (i.e., preparing aqueous dispersions of additives firstly and synthesizing hydrated salt PCMs with corresponding salts subsequently) was also applicable for other functional additives that cannot be directly dispersed well to modify the thermal properties of hydrated salt PCM systems.
DOI	10.1039/c7ra10632g
语种	英语
引用统计
文献类型	期刊论文
条目标识符	http://ir.isl.ac.cn/handle/363002/6374
专题	青海盐湖研究所知识仓储
推荐引用方式 GB/T 7714	Zhang, Xinxing,Li, Xiang,Zhou, Yuan,et al. Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion[J]. RSC ADVANCES,2018,8(2):1022-1029.
APA	Zhang, Xinxing.,Li, Xiang.,Zhou, Yuan.,Hai, Chunxi.,Shen, Yue.,...&Zeng, Jinbo.(2018).Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion.RSC ADVANCES,8(2),1022-1029.
MLA	Zhang, Xinxing,et al."Enhanced thermal conductivity in a hydrated salt PCM system with reduced graphene oxide aqueous dispersion".RSC ADVANCES 8.2(2018):1022-1029.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Enhanced thermal con（3541KB）	期刊论文	出版稿	开放获取	CC BY-NC-SA	浏览请求全文